Specifications

• Base: MS polymer.
• Flow: 5 bar / 3 mm / 23 °C 140 g/min.
• Skin formation: 23 °C 50% R.V. 8 minutes.
• Non-stick: 23 °C 50% R.V. 25 minutes.
• Through-curing: 23 °C 50% R.V.:
  • 24 t – 6 mm
  • 48 t – 7 mm
  • 72 t – 8 mm
• E-module 100%: 172N/cm² /1.72 MPa.
• Specific Resistance: 26.257 GigaOhm/cm.
• Volume creep after curing: <3%.
• Hardness – DIN 53505: 60 Shore A.
• Tensile strength:
  • after 7 days: 260 N/cm²
  • after 1 month: 280 N/cm²
  • after 3 months: 310 N/cm².
• Tear strength – DIN 53504: 140N/cm² /1.40 MPa.
• Ambient temperature for application: between 5 and 40 °C.
• Thermal stability: -40 °C to +90 °C / max: 155 °C max. 30 minutes.
• Elongation at Break – Din 53504: > 350%.
• Air permeability (in accordance with report 3P02093 in SP TRI in Sweden: >0.2 m³/m².
• Non-toxic.
• Water vapour transmission (DIN EN ISO 12572): 1.6.
• Pressure resistance (ISO 11432): 1.19 N/mm².
• Chemical resistance:
  • good: water, seawater, aliphatic solvents, oils, fats, dilute organic acids, lye
  • Moderate: esters, ketones, flavorings.
  • Bad: Concentrated acids, chlorinated solvents, chlorine from swimming pools.
• Shelf life: 18 months from production. The first seven digits of the batch number form the production date: YY WW DDD, where YY = year (19 = 2019), WW = week and DDD = day.